Navegando por Assunto "Aço"

Agora exibindo 1 - 3 de 3

Estudo da influência da temperatura na alteração do revestimento permanente do fundo de uma panela de aço em uma aciaria elétrica
(2022-01-09) Diniz, Emilly Vithória Oliveira Rocha; Diniz, Verônica Cristhina de Souza; http://lattes.cnpq.br/9239037374332331; http://lattes.cnpq.br/4526803179109939
Steel is an iron-carbon alloy, which can be used in the most diverse sectors of the economy due to its low manufacturing cost and its chemical and mechanical properties. Refractory materials are part of the manufacture of steel through the composition of the internal lining in the equipment used in the manufacture of the same. Different types of refractory materials can be applied in these equipments, namely: dolomitic, magnesium, aluminous. In the present work, the modification of the thickness of the permanent coating of the steel ladle will be discussed in order to increase the weight of cast steel, performing the necessary measurements and comparisons to guarantee operational safety, obtaining results within the established limits, enabling the change.
Influência da tensão, velocidade de alimentação e DBCP na resistência à corrosão de revestimentos à base da liga inconel 625 depositada por MIG
(2019-07-09) Lima, Igor Jaloto de; Santos, Aureliano Xavier dos; http://lattes.cnpq.br/0810494477757052
Annually, high investments are made in the maintenance of pipelines used in the oil industry around the globe. Thus, solutions are sought that combine low cost, reproducibility and properties that are consistent, mainly against corrosion. One of these is the use of materials that have high mechanical and anticorrosive properties in the form of coatings, which could be deposited by welding. The objective of this study was to evaluate the effects of different welding parameters on the corrosion resistance of coatings based on the Inconel 625 alloy, deposited by MIG process in API 5L X70 steel. The parameters were optimized using the factorial experimental design and the results analyzed by the Response Surface Methodology (RSM). Three deposits with ½ overlap were performed by MIG welding process, followed by a cross section cut in the samples for analysis of the dilution, iron content and corrosion resistance by linear potentiodynamic polarization (PPL) through corrosion potential (Ecorr), corrosion current (Icorr) and polarization resistance (Rp). The coatings obtained presented values of the dilution ranging from 5.8% to 15.01%. The coating that presented lower dilution value, also was the one with lower Icorr and Fe, besides higher Rp and Ecorr, thus, greater corrosion resistance.
Método espectrofotométrico para determinação de traços de ferros
(1978) Câmara Filho, José Calazans Soares da; Andrade, Pedro Corrêa de Oliveira
A coloração violeta produzida pela reação do ácido carmínioo com íon ferroso pode ser usada para a determinação de ferro. A máxima intensidade de cor do carminato ferroso é obtida no intervalo de pH 6,8 - 7,2, 30 minutos após a adição dos reagentes. 0 complexo tem máxima absorção em torno de 585 nm e coeficiente de extinção molar 20 x 103 . 0 sistema obedece a. lei de Beer para as concentrações de 0,4 - 2,0 ppm com leituras de absorção 0,180 - 0,570. Os íons magnésio, potássio e sódio na razão de 1:100 não interferem no método. 0 ferro pode ser determinado na presença de cádmio ou chumbo na proporção 1:50, de' cobalto 1:20 e zinco 1:10. Dentre os elementos e os compostos estudados, o alumínio' e oxido de titânio são os que mais influenciam, não interferem nas razões 1:0,05 e 1:0,5, respectivamente. Na razão 1:1 a presença de cálcio, cobre, cromo ou vanadato não prejudica a determinação. 0 método foi aplicado em amostras de capim apresentando um desvio médio em torno de 4, 57%, quando comparado aos resultados obtidos pela absorção atômica.